Nafion-threaded MOF laminar membrane with efficient and stable transfer channels towards highly enhanced proton conduction
Yan Wang, Hexiang Gao, Wenjia Wu, Zhuofan Zhou, Zhiwei Yang, Jingtao Wang, Yecheng Zou
Abstract
Porous laminar membranes hold great promise to realize ultrafast ion transfer if efficient and stable transfer channels are constructed in vertical direction. Here, metal-organic framework (MOF) nanosheets bearing imidazole molecules in the pores were designed as building blocks to assemble free-standing MOF laminar membrane. Then, Nafion chains were threaded into the pores induced by electrostatic attraction from imidazole molecules by slowly filtering dilute Nafion solution. We demonstrate that the threaded Nafion chains lock adjacent MOF nanosheets, affording highly enhanced structural stability to the resultant laminar membrane with almost no water swelling. Significantly, abundant acid-base pairs are formed in the pores along Nafion chains, working as efficient, continuous conduction pathways in vertical direction. Proton conductivities as high as 110 and 46 mS·cm−1 are obtained by this membrane under 100% and 40% relative humidity (RH), respectively, which are two orders of magnitude higher than that of pristine MOF membrane. The conductivity under low humidity (40% RH) is even over 2 times higher than that of commercial Nafion membrane, generating the maximum power density of 1,100 mW·cm−2 in hydrogen fuel cell (vs. 291 mW·cm−2 of Nafion membrane). Besides, the influence of water state on proton transfer in confined space is investigated in detail.