Reduced Lattice Thermal Conductivity for Half-Heusler ZrNiSn through Cryogenic Mechanical Alloying
Amin Bahrami, Pingjun Ying, Ulrike Wolff, Nicolás Pérez Rodríguez, Gabi Schierning, Kornelius Nielsch, Ran He
Abstract
The ZrNiSn-based half-Heusler compounds are promising for thermoelectric applications in the mid-to-high temperature range. However, their thermoelectric performance was greatly limited due to the remaining high thermal conductivity, especially the lattice thermal conductivity. Herein, we report the synthesis of pristine half-Heusler ZrNiSn through direct mechanical alloying at a liquid nitrogen temperature (i.e., cryomilling) followed by spark plasma sintering. It is shown that the onset sintering temperature is greatly reduced for the cryomilled powders with a high density. A reduced thermal conductivity is subsequently realized from room temperature to 700 °C in the cryomilled samples than the one that was differently prepared (from 7.3 to 4.5 W/m K at room temperature). The pronounced reduction in thermal conductivity of ZrNiSn yields a maximum zT of ∼0.65 at 700 °C. Our study shows the possibility of cryomilling in advancing the thermoelectric performance through enhanced phonon scattering.