Ultralow Surface Resistance via Vacuum Heat Treatment of Superconducting Radio-Frequency Cavities
S. Posen, A. Romanenko, A. Grassellino, O.S. Melnychuk, D.A. Sergatskov
Abstract
We report on an effort to improve the performance of superconducting radiofrequency cavities by using heat treatment in a temperature range sufficient to dissociate the natural surface oxide. We find that the residual resistance is decreased significantly, and we find an unexpected reduction in the Bardeen-Cooper-Schrieffer (BCS) resistance. Together these result in extremely high-quality factor values at relatively large accelerating fields ${E}_{\mathrm{acc}}$ \ensuremath{\sim} 20 MV/m: ${Q}_{0}$ = 3--4 \ifmmode\times\else\texttimes\fi{} ${10}^{11}$ at 1.5 K and ${Q}_{0}$ \ensuremath{\sim} 5 \ifmmode\times\else\texttimes\fi{} ${10}^{10}$ at 2.0 K. In one cavity, measurements of surface resistance versus temperature showed an extremely small residual resistance of just 0.63 \ifmmode\pm\else\textpm\fi{} 0.06 n\ensuremath{\Omega} at 16 MV/m. Secondary ion mass spectrometry measurements confirm that the oxide is dissociated significantly, but they also show the presence of nitrogen after heat treatment. We also present studies of surface oxidation via exposure to air and to water, as well as the effects of very light surface removal via HF rinse. The study is performed on 1.3 GHz cavities, but the effect may be extendable to other frequencies as well. The possibilities for applications and the planned future development are discussed.