Ru–CeO<sub>2</sub> and Ni–CeO<sub>2</sub> Coated on Open-Cell Metallic Foams by Electrodeposition for the CO<sub>2</sub> Methanation
Phuoc Hoang Ho, Giancosimo Sanghez de Luna, Arturo Poggi, Monica Nota, Enrique Rodrı́guez-Castellón, Giuseppe Fornasari, Angelo Vaccari, Patricia Benito
Abstract
CO2 methanation structured catalysts, made by a layer of Ru–CeO2 or Ni–CeO2 (Ru/Ce = 3/97; Ni/Ce = 1/3 and 3/1) on open-cell NiCrAl foams, are prepared by electrodeposition and a subsequent calcination step. The performance of the catalysts at a space velocity of 320,000 mL gcat–1 h–1 in a feedstock with H2/CO2/N2 = 4/1/1 v/v, significantly depends on the Ni content and the preparation method. A low Ru or Ni content promotes the metal–CeO2 interaction, the formation of defects in CeO2 as well as the development of a lower amount of cracks in the coating; however, the catalysts show a poor CO2 conversion and selectivity to CH4. The CH4 production rate at low temperature largely increases for the high Ni loaded catalyst, 68.7 LCH4 gNi–1 h–1 at 350 °C oven temperature. This productivity is similar to the value obtained with a Ni3Ce1 pellet catalyst prepared by the coprecipitation method, a behavior not achievable for low Ru- and Ni-loaded catalysts.