A novel method for evaluating solidification cracking susceptibility of austenitic stainless steel using trapezoidal hot cracking test during laser welding
Dan Wang, Feng Zhang, Eakkachai Warinsiriruk, Qiang Zhu, Tianqing Li, Hongliang Li, Nan Xu, Ke Han, Zeyu Wang, Shaowei Yang
Topics & Concepts
CrackingMaterials scienceWeldingMetallurgyAusteniteLaserLaser beam weldingAustenitic stainless steelComposite materialCorrosionMicrostructureOpticsPhysicsHydrogen embrittlement and corrosion behaviors in metalsMicrostructure and Mechanical Properties of SteelsWelding Techniques and Residual Stresses