Tuning the Interaction between Platinum Single Atoms and Ceria by Zirconia Doping for Efficient Catalytic Ammonia Oxidation
Wei Tan, Yandi Cai, Haowei Yu, Shaohua Xie, Meiyu Wang, Kailong Ye, Lu Ma, Steven N. Ehrlich, Fei Gao, Lin Dong, Fudong Liu
Abstract
Aiming at the development of an efficient NH 3 oxidation catalyst to eliminate the harmful NH 3 slip from the stationary flue gas denitrification system and diesel exhaust aftertreatment system, a facile ZrO 2 doping strategy was proposed to construct Pt 1 /Ce x Zr 1– x O 2 catalysts with a tunable Pt-CeO 2 interaction strength and Pt–O–Ce coordination environment. According to the results of systematic characterizations, Pt species supported on Ce x Zr 1– x O 2 were mainly in the form of single atoms when x ≥ 0.7, and the strength of the Pt-CeO 2 interaction and the coordination number of Pt–O–Ce bond (CN Pt–O–Ce ) on Pt 1 /Ce x Zr 1– x O 2 showed a volcanic change as a function of the ZrO 2 doping amount. It was proposed that the balance between the reasonable concentration of oxygen defects and limited surface Zr–O x species well accounted for the strongest Pt-CeO 2 interaction and the highest CN Pt–O–Ce on Pt/Ce 0.9 Zr 0.1 O 2 . It was observed that the Pt/Ce 0.9 Zr 0.1 O 2 catalyst exhibited much higher NH 3 oxidation activity than other Pt/Ce x Zr 1– x O 2 catalysts. The mechanism study revealed that the Pt 1 species with the stronger Pt-CeO 2 interaction and higher CN Pt–O–Ce within Pt/Ce 0.9 Zr 0.1 O 2 could better activate NH 3 adsorbed on Lewis acid sites to react with O 2 thus resulting in superior NH 3 oxidation activity. This work provides a new approach for designing highly efficient Pt/CeO 2 based catalysts for low-temperature NH 3 oxidation.