Enhanced Electrocaloric Effect in 0.73Pb(Mg1/3Nb2/3)O3-0.27PbTiO3 Single Crystals via Direct Measurement
Biao Lu, Xiaodong Jian, Xiongwei Lin, Yingbang Yao, Tao Tao, Bo Liang, Haosu Luo, Sheng‐Guo Lu
Abstract
Electrocaloric properties of [110] and [111] oriented 0.73Pb(Mg1/3Nb2/3)O3-0.27PbTiO3 single crystals were studied in the temperature range of 293–423 K. The Maxwell relations and the Landau–Ginsburg–Devonshire (LGD) phenomenological theory were employed as the indirect method to calculate the electrocaloric properties, while a high-resolution calorimeter was used to measure the adiabatic temperature change of the electrocaloric effect (ECE) directly. The results indicate that the directly measured temperature changes of ΔT > 2.5 K at room temperature were procured when the applied electric field was reversed from 1 MV/m to −1 MV/m, which are larger than those deduced pursuant to the Maxwell relation, and even larger than those calculated using the LGD theory in the temperature range of 293–~380 K.