Gelatin/Hyaluronic Acid Photocrosslinked Double Network Hydrogel with Nano-Hydroxyapatite Composite for Potential Application in Bone Repair
Jianuo Zheng, Yunping Wang, Yuwen Wang, Ruiping Duan, Lingrong Liu
Abstract
The application of hydrogels in bone repair is limited due to their low mechanical strength. Simulating bone extracellular matrix, methylacrylylated gelatin (GelMA)/methylacrylylated hyaluronic acid (HAMA)/nano-hydroxyapatite(nHap) composite hydrogels were prepared by combining the double network strategy and composite of nHap in this study. The precursor solutions of the composite hydrogels were injectable due to their shear thinning property. The compressive elastic modulus of the composite hydrogel was significantly enhanced, the fracture strength of the composite hydrogel nearly reached 1 MPa, and the composite hydrogel retained its high water content at above 88%. The composite hydrogels possess good compatibility with BMSCS and have the potential to be used as injectable hydrogels for bone defect treatment.