Tribological properties of hexagonal boron nitride nanoparticles as a lubricating grease additive
Yu Cheng, Yingbin Bu, Pengxi Guan, Yujie Yang, Jianbo Qing
Abstract
Abstract The friction and anti‐wear behaviours of hexagonal boron nitride (h‐BN) nanoparticles as a lithium lubricating grease additive are being investigated under sliding conditions. The grease with 3 wt% 60 nm h‐BN particles and the grease with 1 wt% 500 nm h‐BN particles lead to 22.34% and 20.18% reductions in the wear scar diameter, respectively, although the friction coefficients slightly decrease. The boric acid H 3 BO 3 with layer‐crystal structure produces during the friction process, and the synergistic effect of h‐BN nanoparticles and H 3 BO 3 makes friction reduction and wear‐resistant enhancement. Furthermore, the 60 nm h‐BN particles filled in the asperity valleys of the friction surface make a rolling effect and establish a protective film, while the 500 nm h‐BN particles shield the asperity contact between friction pairs and make a polishing effect as well.