Liquid Regions of Lanthanum-Bearing Aluminosilicates
Yandong Li, Tongsheng Zhang, Yefeng Feng, Chengjun Liu, Maofa Jiang
Abstract
The Al2O3-SiO2, La2O3-Al2O3, and La2O3-SiO2 binary phase diagrams were estimated by Redlich–Kister expression. La4.67Si3O13 (=La4.67(SiO4)3O) was introduced to improve the existing phase diagrams. The Al2O3-SiO2-La2O3 ternary phase diagram extrapolated by Kohler method was optimized. Then, the liquidus of Al2O3-SiO2-La2O3 system at 1600 °C was compared with Al2O3-SiO2-RE2O3 (RE = Rare Earth Elements) systems and experimental results in other literature. The high temperature experiments were conducted in the tube furnace at 1500 °C. Then the field emission scanning electron microscope (FE-SEM), energy dispersive spectrometer (EDS), and X-ray diffraction (XRD) were employed to verify the calculated liquid region and precipitates phase at 1500 °C. Moreover, the liquidus of binary systems were compared with FactSage results and experiments. The optimized ternary phase diagram shows the relatively reliable region of liquid phase, and it is significant to the seal glass of solid oxide fuel cells and other fields being related to RE containing silicates.