Copper-Based Nanomaterials for Fine-Pitch Interconnects in Microelectronics

Abstract

Conspectus Nanostructured copper-based materials have emerged as a new generation of robust architectures for realizing high-performing and reliable interconnection in modern electronic packaging. As opposed to traditional interconnects, nanostructured materials offer better compliance during the packaging assembly process. Due to the high surface area-to-volume ratio of nanomaterials, they also enable joint formation by sintering through thermal compression at much lower temperatures compared to bulk counterparts. Nanoporous Cu (np-Cu) films have been employed in electronic packaging as materials that facilitate a chip-to-substrate interconnection, realized by a Cu-on-Cu bonding after sintering. In this Account, we discuss the use of self-supported np-Cu films for low-temperature joint formation. The novelty of this work comes from the incorporation of tin (Sn) into the np-Cu structure, thus ensuring lower sintering temperatures with a goal of producing Cu–Sn intermetallic alloy-based joints between two Cu substrates. The incorporation of Sn is done using an all-electrochemical bottom-up approach that involves the conformal coating of fine-structured np-Cu (initially formed by dealloying of Cu–Zn alloys) with a thin layer of Sn. This Account provides insight on existing technologies for using nanostructured films as materials for interconnects as well as the optimization studies for the Sn-coating processes as a new alternative approach. The applicability of the synthesized Cu–Sn nanomaterials for low-temperature joint formation is also discussed. To realize this new approach, the Sn-coating process is administered by a galvanic pulse plating technique, which is optimized to preserve the porosity in the structure with a Cu/Sn atomic ratio that allows for the formation of the Cu 6 Sn 5 intermetallic compound (IMC). Nanomaterials obtained using this approach are subjected to joint formation by sintering at temperatures between 300 and 200 °C under 20 MPa pressure in forming gas atmosphere. Cross-section characterization of the formed joints postsintering reveals densified bonds with minimal porosity that consist predominantly of the Cu 3 Sn IMC. Furthermore, these joints are less prone to structural inconsistencies compared to existing joints formed using purely np-Cu. The results presented in this Account provide a glimpse into a facile and cost-effective approach for synthesizing nanostructured Cu–Sn films and illustrate their applicability as new interconnect materials.

Topics & Concepts