Improvement of the piezoelectricity of PVDF-HFP by CoFe2O4 nanoparticles
Dan Lei, Ning Hu, Liangke Wu, Alamusi Alamusi, Huiming Ning, Yang Wang, Zhaonan Jin, Yaolu Liu
Abstract
High piezoelectric composite films composed of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) and ferromagnetic cobalt ferrite (CoFe2O4) (0.00 wt% to 0.2 wt%) are prepared by a solution casting method accompanied by uniaxial stretching and high electric field poling. The decisive effect of the poling electric field on the power generating capability was confirmed by the experiments. For pure PVDF-HFP films, when the maximum electric field Emax is 120 MV/m, the calibrated open circuit voltage reaches 2.93 V, which is much higher than those poled at lower electric fields (70 MV/m: 1.41 V; 90 MV/m: 2.11 V). Furthermore, the addition of CoFe2O4 also influences the piezoelectricity dramatically. In the samples containing 0.15 wt% CoFe2O4, the calibrated open circuit voltage increases to the maximum value of 3.57 V. Meanwhile, the relative fraction of the β-phase and the crystallinity degree are 99% and 48%, respectively. The effects of CoFe2O4 nanoparticles on initial crystallization, uniaxial stretching and high electric field poling are investigated by XRD, FTIR and DSC.