The Impact of a CO2 Laser on the Adhesion and Mold Resistance of a Synthetic Polymer Layer on a Wood Surface
Ladislav Reinprecht, Zuzana Vidholdová
Abstract
In the wood industry, laser technologies are commonly applied for the sawing, engraving, or perforation of solid wood and wood composites, but less knowledge exists about their effect on the joining and painting of wood materials with synthetic polymer adhesives and coatings. In this work, a CO2 laser with irradiation doses from 2.1 to 18.8 J·cm−2 was used for the modification of European beech (Fagus sylvatica L.) and Norway spruce (Picea abies /L./ Karst) wood surfaces—either in the native state or after covering them with a layer of polyvinyl acetate (PVAc) or polyurethane (PUR) polymer. The adhesion strength of the phase interface “synthetic polymer—wood”, evaluated by the standard EN ISO 4624, decreased significantly and proportionately in all the laser modification modes, with higher irradiation doses leading to a more apparent degradation and carbonization of the wood adherent or the synthetic polymer layer. The mold resistance of the polymers, evaluated by the standard EN 15457, increased significantly for the less mold-resistant PVAc polymer after its irradiation on the wood adherent. However, the more mold-resistant PUR polymer was able to better resist the microscopic fungi Aspergillus niger Tiegh. and Penicillium purpurogenum Stoll. when irradiation doses of higher intensity acted firstly on the wood adherent.