Study on the Properties and Structure of Rotationally Moulded Linear Low-Density Polyethylene Filled with Quartz Flour
Karolina Głogowska, Przemysław Pączkowski, Bronisław Samujło
Abstract
The objective of this study is to determine selected properties of thin-walled rotationally moulded composite parts. Linear low-density polyethylene (LLDPE) filled with quartz flour (QF, 5-35 wt.%) was tested. High-density polyethylene functionalized with maleic anhydride (HDPE-g-MA) was used as a compatibility agent. Polymer samples were prepared with and without the compatibility agent (2 wt.% in relation to the QF content). The study investigated the effect of QF content and HDPE-g-MA on the properties of rotationally moulded parts, including their melt flow rate (MFR), thermal properties (DSC and TGA), thermomechanical properties (VST), mechanical and physical properties, microstructure, and geometry. Results showed that the properties of LLDPE/QF with HDPE-g-MA were significantly higher than those of LLDPE/QF without HDPE-g-MA. It was also found that the compatibility agent improved the composite material's thermal stability. This improvement was attributed to interactions occurring between the composite material components due to the use of the compatibility agent. In addition to that, microscopic examination demonstrated that the use of HDPE-g-MA improved miscibility of the composite material components. The composite samples containing HDPE-g-MA had better surface geometry.