Exsolution-enhanced reverse water-gas shift chemical looping activity of Sr2FeMo0.6Ni0.4O6-δ double perovskite
Francesco Orsini, Domenico Ferrero, Salvatore F. Cannone, Massimo Santarelli, Andrea Felli, Marta Boaro, Carla de Leitenburg, Alessandro Trovarelli, Jordi Llorca, Georgios Dimitrakopoulos, Ahmed F. Ghoniem
Abstract
This study investigates the structural evolution and redox characteristics of the double perovskite Sr2FeMo0.6Ni0.4O6-δ (SFMN) during hydrogen (H2) and carbon dioxide (CO2) redox cycles and explores the material performance in the Reverse Water-Gas Shift Chemical Looping (RWGS-CL) reaction. In-situ and ex-situ X-Ray Diffraction (XRD) and High-Resolution Transmission Electron Microscopy (HRTEM) studies reveal that H2 reduction at temperatures above 800 °C leads to the exsolution of bimetallic Ni-Fe alloy particles and the formation of a Ruddlesden-Popper (RP) phase. A core–shell structure with Ni-Fe core and a perovskite oxide shell is formed with subsequent redox cycles, and the resulting material exhibits better performance and high stability in the RWGS-CL process. Thermogravimetric (TGA) and Temperature Programmed Reduction (TPR) and Oxidation (TPO) analyses show that the optimal reduction and oxidation temperatures for maximizing the CO yield are around 850 °C and 750 °C respectively, and that the cycled material is able to work steadily under isothermal conditions at 850 °C.