Ruthenium Catalysts Templated on Mesoporous MCM-41 Type Silica and Natural Clay Nanotubes for Hydrogenation of Benzene to Cyclohexane
А. P. Glotov, А. В. Вутолкина, А. А. Pimerzin, V. V. Nedolivko, G. O. Zasypalov, V. D. Stytsenko, Э. А. Караханов, В. А. Винокуров
Abstract
Mesoporous ruthenium catalysts (0.74–3.06 wt%) based on ordered Mobil Composition of Matter No. 41 (MCM-41) silica arrays on aluminosilicate halloysite nanotubes (HNTs), as well as HNT-based counterparts, were synthesized and tested in benzene hydrogenation. The structure of HNT core-shell silica composite-supported Ru catalysts were investigated by transmission electron microscopy (TEM), X-ray fluorescence (XRF) and temperature-programmed reduction (TPR-H2). The textural characteristics were specified by low-temperature nitrogen adsorption/desorption. The catalytic evaluation of Ru nanoparticles supported on both the pristine HNTs and MCM-41/HNT composite in benzene hydrogenation was carried out in a Parr multiple reactor system with batch stirred reactors (autoclaves) at 80 °C, a hydrogen pressure of 3.0 MPa and a hydrogen/benzene molar ratio of 3.3. Due to its hierarchical structure and high specific surface area, the MCM-41/HNT composite provided the uniform distribution and stabilization of Ru nanoparticles (NPs) resulted in the higher specific activity and stability as compared with the HNT-based counterpart. The highest specific activity (5594 h−1) along with deep benzene hydrogenation to cyclohexane was achieved for the Ru/MCM-41/HNT catalyst with a low metal content.