Importance of Electric-Field-Independent Mobilities in Thick-Film Organic Solar Cells
Carr Hoi Yi Ho, Yusen Pei, Yunpeng Qin, Chujun Zhang, Zhengxing Peng, Indunil Angunawela, Austin L. Jones, Hang Yin, Hamna F. Iqbal, John R. Reynolds, Kenan Gündoğdu, Harald Ade, Shu Kong So, Franky So
Abstract
In organic solar cells (OSCs), a thick active layer usually yields a higher photocurrent with broader optical absorption than a thin active layer. In fact, a ∼300 nm thick active layer is more compatible with large-area processing methods and theoretically should be a better spot for efficiency optimization. However, the bottleneck of developing high-efficiency thick-film OSCs is the loss in fill factor (FF). The origin of the FF loss is not clearly understood, and there a direct method to identify photoactive materials for high-efficiency thick-film OSCs is lacking. Here, we demonstrate that the mobility field-dependent coefficient is an important parameter directly determining the FF loss in thick-film OSCs. Simulation results based on the drift–diffusion model reveal that a mobility field-dependent coefficient smaller than 10–3 (V/cm)−1/2 is required to maintain a good FF in thick-film devices. To confirm our simulation results, we studied the performance of two ternary bulk heterojunction (BHJ) blends, PTQ10:N3:PC71BM and PM6:N3:PC71BM. We found that the PTQ10 blend film has weaker field-dependent mobilities, giving rise to a more balanced electron–hole transport at low fields. While both the PM6 blend and PTQ10 blend yield good performance in thin-film devices (∼100 nm), only the PTQ10 blend can retain a FF = 74% with an active layer thickness of up to 300 nm. Combining the benefits of a higher JSC in thick-film devices, we achieved a PCE of 16.8% in a 300 nm thick PTQ10:N3:PC71BM OSC. Such a high FF in the thick-film PTQ10 blend is also consistent with the observation of lower charge recombination from light-intensity-dependent measurements and lower energetic disorder observed in photothermal deflection spectroscopy.