Chelation Effect Induced Robust Biomass Protective Layer for Aqueous Zn Metal Anode
Hao Wu, Hongting Yin, Jin‐Lin Yang, Ruiping Liu
Abstract
Abstract The detrimental dendrite growth and hydrogen evolution corrosion on Zn metal anode greatly hinder the implement of aqueous zinc batteries. Constructing a stable solid electrolyte interphase (SEI) on Zn anode is considered an effective strategy to prolong the cells life. Herein, by using poly(N‐[2‐(3,4‐dihydroxyphenyl)ethyl]‐2‐methylacrylamide) (PDMA) as a case study, the impact of Zn 2+ chelation effect on SEI layer generation is systematically investigated. The DMA monomer tends to form a robust PDMA layer on Zn anode with a higher crosslinking degree with the assistant of Zn 2+ . The Zn─O interaction between Zn metal and PDMA guarantees the long‐term protection efficiency of the SEI layer and uniformizes the Zn nucleation. Moreover, the Zn 2+ desolvation can be propelled by the zincophilic hydroxyl groups in PDMA. As expected, the Zn symmetric cell with in‐PDMA showcases an extended lifespan of over 3800 h. The Zn||NVO full cell maintains a capacity of 150 mAh g −1 after 1000 cycles at 1 A g −1 . This work is believed to guide the future aqueous Zn anode design based on the protective layer engineering.