Fabrication and Photocatalytic Activity of Ag3PO4/T-ZnOw Heterostructures
Jianke Tang, Rongqian Meng, Qi Wang, Shengjian Zhang, Qiaoling Li
Abstract
Abstract The Ag 3 PO 4 /tetrapod-like ZnO whisker (T-ZnOw) heterostructures were prepared via a simple precipitation method. The obtained heterostructures were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-Vis diffuse reflectance spectroscopy. The photodegradation activity of Ag 3 PO 4 /T-ZnOw was evaluated by the degradation of Rhodamine B (RhB) under visible light irradiation. When the molar ratio of Ag 3 PO 4 to T-ZnOw was 10% (Ag 3 PO 4 /T-ZnOw-2), the highest degradation efficiency (92.9%) could be achieved among the heterostructures. The photodegradation rate constant of Ag 3 PO 4 /T-ZnOw-2 (0.05179 min −1 ) was 3.59 times that of T-ZnOw (0.01444 min −1 ). Besides, the Ag 3 PO 4 /T-ZnOw-2 photocatalyst still possessed a degradation efficiency of 77.8% after four successive cycles. The Ag 3 PO 4 /T-ZnOw-2 catalyst had much higher photocatalytic activity than pure T-ZnOw and better stability and reusability than pure Ag 3 PO 4 . The effect of different scavengers on degradation efficiency was investigated, and the possible photocatalytic mechanism of the Ag 3 PO 4 /T-ZnOw photocatalyst was also put forward.