Towards weathering and corrosion resistant, self-warning and self-healing epoxy coatings with tannic acid loaded nanocontainers
Jinke Wang, Weimin Tan, Hao Yang, Xingxing Rao, Xinliang Luo, Lingwei Ma, Chenhao Ren, J.M.C. Mol, Dawei Zhang
Abstract
Abstract In this work, an active protective epoxy coating with weathering resistant, corrosion-warning, and self-healing properties was developed by incorporating tannic acid (TA) loaded mesoporous silica (MSN-TA) nanocontainers. The introduction of MSN-TA nanocontainers could alleviate the coating degradation via scavenging the radicals generated during UV irradiation. Compared with the blank coating, the coating containing 5 wt.% MSN-TA nanocontainers exhibited much less degradation in surface morphology, wettability and glossiness, and maintained a good barrier property after 384 h of accelerated weathering. Once the coating was damaged, the released TA could react with the Fe 3+ ions to form a chelate that endowed the coating scratch with a visible black coloration, i.e. triggering a self-warning capability to indicate the initial onset of corrosion. In addition, the generated chelate could inhibit extensive corrosion propagation, offering a significant self-healing effect demonstrated by the stabilized impedance modulus values during 28 days of immersion in NaCl solution.