Fabrication and Magneto-Optical Property of (Dy0.7Y0.25La0.05)2O3 Transparent Ceramics by PLSH Technology
Ding Zhou, Xiaohui Li, Tun Wang, Jiayue Xu, Zhanyong Wang, Ying Shi, Д. А. Пермин, Stanislav Balabanov
Abstract
(Dy0.7Y0.25La0.05)2O3 magneto-optical transparent ceramics were successfully fabricated by pressureless sintering in reductive H2 atmosphere (PLSH). The raw powder of (Dy0.7Y0.25La0.05)2O3 was synthesized by a modified self-propagating high-temperature synthesis (SHS) and sintered to transparent ceramics at 1400–1600 °C in a flowing H2 atmosphere, showing good sinterability of the as-synthesized raw powder. The magneto-optical Verdet constant of (Dy0.7Y0.25La0.05)2O3 transparent ceramics was measured to be −191.57 rad/(T·m) at a wavelength of 632.8 nm. In this magneto-optical material of (Dy0.7Y0.25La0.05)2O3, relative cheaper Dy and Y were used to replace Tb, and the low cost and good magneto-optical property showed the advantage of application on Faraday isolators (FIs) and Faraday rotators (FRs).