0.68% of solar-to-hydrogen efficiency and high photostability of organic-inorganic membrane catalyst
Wei Li, Wen Duan, Guocheng Liao, Fanfan Gao, Yusen Wang, Rongxia Cui, Jincai Zhao, Chuanyi Wang
Abstract
Solar-driven flat-panel H2O-to-H2 conversion is an important technology for value-added solar fuel production. However, most frequently used particulate photocatalysts are hard to achieve stable photocatalysis in flat-panel reaction module due to the influence of mechanical shear force. Herein, a highly active CdS@SiO2-Pt composite with rapid CdS-to-Pt electron transfer and restrained photoexciton recombination was prepared to process into an organic-inorganic membrane by compounding with polyvinylidene fluoride (PVDF). This PVDF networked organic-inorganic membrane displays high photostability and excellent operability, achieving improved simulated sunlight-driven alkaline H2O-to-H2 conversion activity (213.48 mmol m−2 h−1) following a 0.68% of solar-to-hydrogen efficiency. No obvious variation in its appearance and micromorphology was observed even being recycled for 50-times, which considerably outperforms the existing membrane photocatalysts. Subsequently, a homemade panel H2O-to-H2 conversion system was fabricated to obtain a 0.05% of solar-to-hydrogen efficiency. In this study, we opens up a prospect for practical application of photocatalysis technology. Solar-driven flat-panel H2O-to-H2 conversion is an important technology for value-added solar fuel production. Here, an organic-inorganic interface membrane catalyst displays high photostability and operability with 0.68% solar-to-hydrogen efficiency.