Interplay of Hydrophobic Thiol and Polar Epoxy Silicate Groups on Microstructural Development in Low-Alcohol, Crosslinked Sol–Gel Coatings for Corrosion Prevention
Shegufta Shetranjiwalla, Andrew J. Vreugdenhil, Oliver K.L. Strong
Abstract
We have demonstrated that our patented, crosslinked, sol–gel, epoxy–thiol silicates made from the combination of (a) tetraethoxysilane (TEOS, T), 3-glycidoxypropyltrimethoxysilane (GPTMS, G), and the (b) sulfur-containing 3-mercaptopropyltrimethoxysilane (MPTMS, S) with TEOS in a 1:1 stoichiometric ratio form the 1:1 TGST (crosslinked epoxy and thiol silicates) coating, which can be successfully utilized for the corrosion protection of low-carbon steel. Alcohols that are a by-product of sol–gel reactions influence the network formation, crosslinking density, and formulation stability, are volatile organic contents, and are regulated in the coatings industry. To improve environmental sustainability, a series of low-alcohol (LA) formulations with TG:ST ratios of 3:1 to 1:3 was prepared to investigate the microstructural development and crosslinking reactions emerging from the interplay of the hydrophobic thiol and polar epoxy silicates induced by the low-alcohol environment. The impact on crosslinking density was characterized by Fourier Transform Infrared (FTIR), Raman, XPS, viscosity, and pot-life measurements. Low-alcohol TGST (LA(TGST)) formulations were compared, using the example of 1:1 TGST, to corresponding TGST formulations where alcohols were retained. The reduced impact of LA(TGST) formulations on global warming was quantified. The glossy and scratch-resistant LA(TGST) coatings showed 71% enhanced corrosion protection compared to the non-crosslinked hybrids.