Effect of MWCNTs on Wear Behavior of Epoxy Resin for Aircraft Applications
Mateusz Mucha, Aneta Krzyżak, Ewelina Kosicka, Emerson Coy, Mikołaj Kościński, Tomasz Sterzyński, Michał Sałaciński
Abstract
The aim of the study is to assess the effect of multi-walled carbon nanotubes (MWCNTs) on the wear behavior of MWCNT-doped epoxy resin. In this study, a laminating resin system designed to meet the standards for motor planes was modified with MWCNTs at mass fractions from 0.0 wt.% to 2.0 wt.%. The properties of the carbon nanotubes were determined in Raman spectroscopy and HR-TEM. An examination of wear behavior was conducted on a linear abraser with a visual inspection on an optical microscope and SEM imaging, mass loss measurement, and evaluation of the wear volume on a profilometer. Moreover, the mechanical properties of MWCNTs/epoxy nanocomposite were evaluated through a tensile test and Shore D hardness test. The study shows that the best wear resistance is achieved for the mass percentage between 0.25 wt.% and 0.5 wt.%. For the same range, the tensile strength reaches the highest values and the hardness the lowest values. Together with surface imaging and a topography analysis, this allowed describing the wear behavior in the friction node and the importance of the properties of the epoxy nanocomposite.