Biodegradable PMMA coated Zn–Mg alloy with bimodal grain structure for orthopedic applications - A promising alternative
Alia A. Diaa, Nahed El Mahallawy, Madiha Shoeib, Flavien Mouillard, Tom Ferté, Patrick Masson, Adele Carradò
Abstract
The study examines the impact of microstructure and polymethyl methacrylate (PMMA) grafting on the degradability of Zn-Mg alloys. The mechanical properties of a Zn alloy containing 0.68 wt% Mg and extruded at 200 °C are enhanced for degradable load-bearing applications, addressing a crucial need in the field. The material exhibits a bimodal grain size distribution that is random texture, consisting of secondary phases, grains, and sub-grains. With an elongation to failure of 16 %, the yield and ultimate tensile strengths are 325.9 and 414.5 MPa, respectively, and the compressive yield strength is 450.5 MPa. The "grafting-from" method was used to coat a few micrometers thick of PMMA on both bulk and scaffold Zn alloys to mitigate the corrosion rate. The last one is a porous structure, with a porosity of 65.8 %, considered as in the first approach of an orthopedic implant. After being immersed for 720 h, the PMMA-grafted bulk alloy's corrosion rate decreased from 0.43 to 0.25 mm/y. Similarly, the scaffold alloy's corrosion rate reduced from 1.24 to 0.49 mm/y. These results indicate that the method employed could be used for future orthopedic applications.