Effect of High-k Passivation Layer on High Voltage Properties of GaN Metal-Insulator-Semiconductor Devices
Yutao Cai, Yang Wang, Ye Liang, Yuanlei Zhang, Wen Liu, Huiqing Wen, Ivona Z. Mitrović, Cezhou Zhao
Abstract
In this paper, the GaN-based MIS-HEMTs with Si <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> N <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> single-layer passivation, Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /SiN <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> bilayer passivation, and ZrO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> /SiN <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> bilayer passivation are demonstrated. High-k dielectrics are adopted as the passivation layer on MIS-HEMTs to suppress the shallow traps on the GaN surface. Besides, high permittivity dielectrics passivated MIS-HEMTs also show an improved breakdown voltage characteristic, and that is explained by 2-D simulation analysis. The fabricated devices with high-k dielectrics/SiN <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> bilayer passivation exhibit higher power properties than the devices with plasma enhanced chemical vapor deposition-SiNx single layer passivation, including smaller current collapse and higher breakdown voltage. The Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /SiN <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> passivated MIS-HEMTs exhibit a breakdown voltage of 1092 V, and the dynamic R <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> is only 1.14 times the static R <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> after off-state VDS stress of 150 V. On the other hand, the ZrO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> /SiN <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> passivated MIS-HEMTs exhibit a higher breakdown voltage of 1207 V, and the dynamic Ron is 1.25 times the static R <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> after off-state VDS stress of 150 V.