Improving the connectivity of MgB<sub>2</sub> bulk superconductors by a novel liquid phase sintering process
Guillaume Matthews, Tayebeh Mousavi, Sangeeta Santra, C.R.M. Grovenor, Patrick S. Grant, Susannah Speller
Abstract
Abstract This work investigates a new processing method developed to improve the connectivity of ex-situ MgB 2 bulks at low sintering temperatures. Mg additions (1–10 wt.%) were mixed to pre-synthesised MgB 2 to make composite powders that were sintered at 900 ∘ C by the field assisted sintering technique. Addition of 10 wt.% Mg resulted in a substantial increase in density from 68% to 79% and a dramatic reduction in MgB 4 from 11 to ∼0 wt.%. Pressure and dilatometry data recorded in-situ during the sintering process revealed that Mg additions led to different sintering mechanisms depending on the Mg fraction. For large Mg fractions (6 and 10 wt.%) a Mg liquid phase was formed and led to significant density improvements, and all pre-existing MgB 4 was transformed into MgB 2 . A small amount of residual Mg remained in the bulks after the sintering process. Connectivity was improved with Mg additions, increasing four fold in the 10 wt.% Mg-MgB 2 sample compared to unmodified MgB 2 . J c values at low field were also significantly improved by Mg additions, in particular the 6 and 10 wt.% Mg-MgB 2 specimens showed J c (20 K, 0 T) values 4–5 times higher than for unmodified MgB 2 .