Effect of Denture Disinfectants on the Mechanical Performance of 3D-Printed Denture Base Materials
Nora Alkaltham, Reem Aldhafiri, Ahmad M. Al‐Thobity, Hassan Alramadan, Hussain J Aljubran, Ijlal Shahrukh Ateeq, Soban Q. Khan, Sultan Akhtar, Mohammed M. Gad
Abstract
Denture care and maintenance are necessary for both denture longevity and underlying tissue health. However, the effects of disinfectants on the strength of 3D-printed denture base resins are unclear. Herein, distilled water (DW), effervescent tablet, and sodium hypochlorite (NaOCl) immersion solutions were used to investigate the flexural properties and hardness of two 3D-printed resins (NextDent and FormLabs) compared with a heat-polymerized resin. The flexural strength and elastic modulus were investigated using the three-point bending test and Vickers hardness test before (baseline) immersion and 180 days after immersion. The data were analyzed using ANOVA and Tukey’s post hoc test (α = 0.05), and further verified by using electron microscopy and infrared spectroscopy. The flexural strength of all the materials decreased after solution immersion (p < 0.001). The effervescent tablet and NaOCl immersion reduced the flexural strength (p < 0.001), with the lowest values recorded with the NaOCl immersion. The elastic modulus did not significantly differ between the baseline and after the DW immersion (p > 0.05), but significantly decreased after the effervescent tablet and NaOCl immersion (p < 0.001). The hardness significantly decreased after immersion in all the solutions (p < 0.001). The immersion of the heat-polymerized and 3D-printed resins in the DW and disinfectant solutions decreased the flexural properties and hardness.