Crystal Structures and Microwave Dielectric Properties of Novel MgCu2Nb2O8 Ceramics Prepared by Two-Step Sintering Technique
Sen Peng, Chen Li, Chao Tang, Sheng Liu, Shengxiang Huang, Lei‐Lei Qiu, Lianwen Deng
Abstract
In this work, novel MgCu2Nb2O8 (MCN) ceramics were synthesized by the two-step sintering (TSS) technique, and the phase composition, crystal structures, and microwave dielectric properties were comprehensively studied. X-ray diffraction (XRD) and Raman analysis demonstrated that MCN ceramics are multi-phase ceramics consisting of MgNb2O6 and CuO phases. X-ray photoelectron spectroscopy (XPS) was utilized to investigate the chemical composition and element valence of MgCu2Nb2O8 ceramics. Scanning electron microscopy (SEM) analysis demonstrated dense microstructures in the MCN ceramics prepared at a sintering temperature of 925 °C. The microwave dielectric properties were largely affected by the lattice vibrational modes and densification level of the ceramics. The outstanding microwave dielectric properties of εr = 17.15, Q × f = 34,355 GHz, and τf = −22.5 ppm/°C were obtained for the MCN ceramics sintered at 925 °C, which are results that hold promise for low temperature co-fired ceramic (LTCC) applications.