Effects of different nano size and bulk WO3 enriched by HDPE composites on attenuation of the X-ray narrow spectrum
Amro Obeid, Balaa El, Samad El, Zainab Alsayed, R. Awad, Mohamed S. Badawi
Abstract
The X-rays of the narrow-spectrum N-series ranging from 40 kV to 150 kV were used to determine the radiation attenuation ability of a new category of a polymer composite fabricated for shielding purposes. High density polyethylene was synthesized through a compression molding technique, and incorporated with various filler amounts (10, 15, 25, and 35 wt.%) of bulk micro-sized WO 3 (Sample A), two WO 3 nanoparticles 45 nm (Sample B), and 24 nm (Sample C). The WO 3 filler was identified and characterized using X-ray diffraction and a transmission electron microscope. The mass distribution of the chemical elements of the synthesized composites was determined by energy dispersive X-ray analysis. The obtained results of the different attenuation parameters revealed that the particle size and weight fraction of WO particles have an outstanding effect on the X-ray shielding ability of this composite. The 3 experimental measurements of the mass attenuation coefficients were compared to the theoretical values tabulated in the NIST databases XCOM and FFAST. The mass attenuation coefficient was increased with the increment of WO 3 wt.% as well as with the decrease of the WO 3 particle size. This improvement in the attenuation parameters of the NP(C) composite suggests their promising applications in radiation protection at the diagnostic level.