Electrospun composites nanofibers from cellulose acetate/carbon black as efficient adsorbents for heavy and light machine oil from aquatic environment
Nehad A. Elmaghraby, Ahmed M. Omer, El‐Refaie Kenawy, Mohamed Gaber, Ahmed El Nemr
Abstract
Abstract The feasibility of preparing cellulose acetate/carbon black (CA/CB) composite nanofiber in one step through electrospinning process and investigating its potential oil absorbability and application for machine oil removal from aquatic environment was reported. Different CA/CB composite nanofibers were fabricated by electrospinning of cellulose acetate (CA) solution containing different loads of 0.7, 1.5, and 2.2% CB relative to the weight of CA and labeled as CA/CB0.7, CA/CB1.5, and CA/CB2.2. The scanning electron microscope (SEM) images showed continuous and smooth fiber with submicron diameter ranging from 400–900 nm with good adhering of CB into CA nanofiber. Furthermore, the CA/CB composite nanofibers exhibited high surface area compared with CA nanofiber, which reached 3.057, 2.8718 and 8.244 m 2 /g for CA/CB0.7, CA/CB1.5 and CA/CB2.2, respectively. Oil adsorption tests were performed with heavy and light machine oils. The CA/CB composite nanofibers showed higher affinity for oil removal from an aqueous solution than pure CA nanofiber. The CA/CB1.5 composite nanofiber has an exceptional performance for the adsorption of both oils, and the maximum oil adsorbed reached 10.6 and 18.3 g/g for light and heavy machine oils, respectively. The kinetic of machine oils adsorption was fitted well by the pseudo-second-order model. Besides, CA/CB composite nanofiber exposed good adsorption properties and respectable reusability after regeneration for four consecutive cycles. The results advocate the excellent potential of as-fabricated CA/CB composite nanofiber as a promising reusable oil adsorbent for oil spill cleanup applications.