Fluorinated High-Voltage Electrolytes To Stabilize Nickel-Rich Lithium Batteries

Abstract

As state-of-the-art (SOA) lithium-ion (Li-ion) batteries approach their specific energy limit (∼250 Wh kg –1 ), layer-structured, nickel-rich (Ni-rich) lithium transition metal oxide-based cathode materials, e.g., LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811), have attracted great interest owing to their practical high specific capacities (>200 mAhg –1 ). Coupled with their high average discharge voltages (∼4 V vs Li/Li + ), Ni-rich cathode-based lithium batteries possess a great potential to achieve much higher specific energies (>350 Wh kg –1 at the cell level) than the SOA Li-ion counterparts. In addition, Ni-rich oxides are low-cost battery cathode materials due to their low cobalt contents. However, Ni-rich cathode-based lithium batteries suffer quick capacity degradations upon cycling, particularly at high upper cutoff voltages (e.g., ≥4.5 V vs Li/Li + ), due to crystal structure changes of the active cathode materials and parasitic side reactions at the electrolyte/electrode interfaces. In this study, a fluorinated-solvent-based, high-voltage stable electrolyte (HVE), i.e., 1 M Li bis(trifluoromethanesulfonyl)imide (LiTFSI) in fluoroethylene carbonate (FEC), bis(2,2,2-trifluoroethyl) carbonate (FDEC), and methyl (2,2,2-trifluoroethyl) carbonate (FEMC) with Li difluoro(oxalate)borate (LiDFOB) additive, was formulated and evaluated in Li/NMC811 battery cells. To the best of our knowledge, this class of electrolyte has not been investigated for Ni-rich cathode-based lithium batteries. Li/NMC811 cells with HVE exhibited a superior long-term cycle performance stability, maintaining ∼80% capacity after ∼500 cycles at a high cutoff voltage of 4.5 V (vs Li/Li + ) than a baseline carbonate-solvent-based electrolyte (BE). The superior cycle stability of the Li/NMC811 cells is attributed to the inherently high-voltage stability of HVE, supported by the physical and electrochemical analyses. This conclusion is supported by our density functional theory (DFT) modeling where HVE shows a less tendency of deprotonation/oxidation than BE, leading to the observed cycle stability. The findings in this study are important to help tackle the technical challenges facing Ni-rich cathode-based lithium batteries to realize their high energy density potentials with a long cycle life.

Topics & Concepts