High piezoelectricity induced by lattice distortion and domain realignment in Li<sub>2</sub>CO<sub>3</sub>-added lead-based ceramics
Hao Chen, Yining Xie, Jingwen Xi, Wanfeng Zhuang, Weiling Wang, Jie Xing, Hong Liu, Jianguo Zhu
Abstract
The 0.2Pb(Ni 1/3 Nb 2/3 )O 3 –0.1Pb(Zn 1/3 Nb 2/3 )O 3 –0.7Pb(Zr 0.46 Ti 0.54 )O 3 + x wt% Li 2 CO 3 ceramics were synthesized by the solid–state reaction method.
Topics & Concepts
PiezoelectricityCeramicMaterials scienceLattice (music)Solid-stateDistortion (music)CrystallographyChemistryAnalytical Chemistry (journal)Physical chemistryPhysicsOptoelectronicsMetallurgyComposite materialAmplifierAcousticsCMOSChromatographyFerroelectric and Piezoelectric MaterialsMicrowave Dielectric Ceramics SynthesisAcoustic Wave Resonator Technologies