The structural properties of Y1-XLaXBa4Cu7O15+ δ superconductor compound
Auday H. Shaban, L. A. Mohammed, Hala S. Hussein, General Directorate of Karbala Education, Karbala, Iraq, K. A. Jasim
Abstract
The eff ect of partial substitution for lanthanum (La) on the structural properties of the compound Y1-xLaxBa4Cu7O15+δ were studied. The variation of (x) are x=0.1, 0.2 and 0.3, which was synthesized by solid state reaction method. The mixed powder was pressed with pressure (7 ton / cm2) as a disc (1.5 cm) diameter and a thickness of (0.25 to 0.3 cm). The samples were sintering by 120 °C / hour with a changing rate from room temperature to 850 ° C through 72 hours. XRD analysis using to calculate crystal size, strain and degree of crystallinity. It was found all samples have orthorhombic structure and change of structure with increasing lanthanum concentration. It was shown that the change lanthanum concentrations of all our samples produce a change in the crystal size, strain, degree of crystallinity and lattice parameters.