Enhancing Self-Healing and Adhesion Bonding Properties: Investigating the Promising Potential of Ce-ZIF8 MOF Hybrid Thin Films as pH-Responsive Nanocoatings
Mozhgan Falahaty marvast, Mahsa Gholambargani, Mohammad Ramezanzadeh, Bahram Ramezanzadeh
Abstract
Further modification of the pre-treated steel surface with cerium conversion coating was performed using a novel porous coordination polymer (PCP) based on zeolitic imidazole framework-8 (ZIF8) in order to reduce the defect and disorders of the surface. The treated mild steels (MS) with Ce (MS/Ce) and Ce-ZIF8 (MS/Ce-ZIF8) were characterized by the GIXRD, Raman, and FT-IR, and via contact angle and FE-SEM, their surface features were investigated. The protection performance of the samples against corrosion was evaluated in the saline solution media using electrochemical impedance spectroscopy (EIS, in the long term) and polarization tests. The results evidenced that applying the ZIF8 nanoparticles onto the Ce-treated steel surface increased the total resistance value after 24 h of immersion (49.47%). Afterward, the ZIF8-modified coating (MS/Ce and MS/Ce-ZIF8) impact on the epoxy coating protection function was characterized by EIS (in the scratched form), salt spray (5 wt % salts), cathodic disbonding (at 25 °C), and pull-off tests. The EIS outcomes of the scratched coatings proved approximately a 51.29% increase in R t of the MS/Ce-ZIF8/EC sample compared with the MS/EC sample after 24 h of immersion. The cathodic disbonding test results after 24 h of exposure revealed that the delamination area of the coating decreased in the modified sample, and the delamination radius of the epoxy coating was about 4.78, 2.96, and 2.0 mm for the MS/EC, MS/Ce/EC, and MS/Ce-ZIF8/EC samples, respectively.