Influence of Laser Polishing on the Material Properties of Aluminium L-PBF Components
Markus Hofele, A. Roth, Patrick Hegele, Tim Schubert, Jochen Schanz, David K. Harrison, A.K.M. De Silva, Harald Riegel
Abstract
In this study, the influence of laser polishing on the microstructural and mechanical properties of additively manufactured aluminium AlSi10Mg Laser Powder Bed Fusion (L-PBF) parts is analysed. The investigation is carried out on a 5-axis laser cell equipped with 1D Scanner optics driven by a solid-state disc laser at a wavelength of 1030 nm. Laser polishing is performed with pulsed or continuous laser radiation on samples in the initial L-PBF state or after stress relief treatment in a furnace. The metallurgical investigation of the remelting zone with a depth of 101–237 µm revealed an unchanged and homogeneous chemical composition, with a coarsened α-phase and a changed grain structure. The hardness within the remelting zone is reduced to 102–104 HV 0.1 compared to 146 HV 0.1 at the L-PBF initial state. Below the remelting zone, within the heat affected zone, a reduced microhardness, which can reach a thickness up to 1.5 mm, occurs. Laser polishing results in a reduction in residual stresses and resulting distortions compared to the L-PBF initial state. Nevertheless, the re-solidification shrinkage of the polished surface layer introduces additional tensions, resulting in sample distortions well above ones remaining after a stress relieve heat treatment of the initial state. The mechanical properties, analysed on laser polished flat tensile specimens, revealed an increase in the ultimate elongation from 4.5% to 5.4–10.7% and a reduction in the tensile strength from 346 N/mm2 to 247–271 N/mm2 through laser polishing. Hence, the strength resulting from this is comparable to the initial L-PBF specimens after stress relieve heat treatment.