Achievement of Both Mechanical Properties and Intrinsic Self-Healing under Body Temperature in Polyurethane Elastomers: A Synthesis Strategy from Waterborne Polymers
Liangdong Zhang, Teng Qiu, Xiting Sun, Longhai Guo, Lifan He, Jun Ye, Xiaoyu Li
Abstract
Inspired by the growing demand for smart and environmentally friendly polymer materials, we employed 2,2'-disulfanediyldianiline (22DTDA) as a chain extender to synthesize a waterborne polyurethane (WPUR). Due to the ortho-substituted structure of the aromatic disulfide, the urea moieties formed a unique microphase structure in the WPUR, its mechanical strength was enhanced more 180 times relative to that of the material prepared without 22DTDA, and excellent self-healing abilities at body temperature in air or under ultrasound in water were obtained. If the self-healing process was carried out at 37 °C, 50 °C or under ultrasound, the ultimate tensile strength and elongation at break of the healed film could reach 13.8 MPa and 1150%, 15.4 MPa and 1215%, or 16 MPa and 1056%, respectively. Moreover, the WPUR films could be re-healed at the same fracture location over three cutting-healing cycles, and the recovery rates of the tensile strength and elongation at break remained almost constant throughout these cycles.