The study on adsorption behavior of 2,4-DCP in solution by biomass carbon modified with CTAB-KOH
Dajun Ren, Hou–Yong Yu, Jian Wu, Zhaobo Wang, Shuqin Zhang, Xiaoqing Zhang, Xiangyi Gong
Abstract
In this study, rice straw was used to prepare biomass carbon, which was modified with KOH and cetyltrimethylammonium bromide (CTAB) to obtain modified biomass carbon (MBC). The biomass carbon (BC) before and after modification was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FT-IR), and the surface morphology, crystal structure and surface group characteristic BC were explored. The specific surface area and micropores of the modified biomass carbon increased significantly, the crystallinity was higher, and the pore structure was more clearly found. The adsorption performance of MBC for 2,4-dichlorophenol (2,4-DCP) was investigated. The results showed that under the best adsorption conditions ((2,4-DCP concentration (200 mg/L), MBC dosage (50 mg), pH (5.5), and loading time (60 min), temperature (room temperature)), the removal rate of 2,4-DCP was up to 42.5%, and adsorption capacity was 85.13 mg/g. The adsorption of 2,4-DCP on MBC materials was better explained by the pseudo-second-order kinetic model and the Langmuir adsorption isotherm model. It was believed that the adsorption of 2,4-DCP by MBC was the monolayer adsorption process on the uniform surface of MBC at high concentration, and there was no interaction between the 2,4-DCP and MBC adsorbate during this process.