Novel Biocompatible Zr-Based Alloy with Low Young’s Modulus and Magnetic Susceptibility for Biomedical Implants
Renhao Xue, Dong Wang, Dawei Yang, Ligang Zhang, Xiaoning Xu, Libin Liu, Di Wu
Abstract
The microstructure, mechanical properties, magnetic susceptibility, electrochemical corrosion performance, in vitro cell compatibility and blood consistency of Zr-16Nb-xTi (x = 0, 4, 8, 12 and 16 wt.%) materials were investigated as potential materials for biomedical implants. X-ray diffraction (XRD) and Transmission electron microscopy (TEM) analyses revealed the secondary phase martensite α' formed during the quenching process. The phase composition contained metastable β and martensite α', resulting from Ti addition. These phase constitutions were the main causes of a low Young's modulus and magnetic susceptibility. The in vitro cytocompatibility analysis illustrated that the MG63 cells maintained high activity (from 91% to 97%) after culturing in Zr-16Nb-xTi extraction media for 12 days due to the high internal biocompatibility of Zr, Nb and Ti elements, as well as the optimal corrosion resistance of Zr-16Nb-xTi. On the basis of Inductively coupled plasma optical emission spectrometry (ICP-OES) ion release studies, the concentration of Zr, Nb and Ti was noted to reach the equipment detective limit of 0.001 mg/L, which was much lower than pure Ti. With respect to the corrosion behavior in Hank's solution, Zr-16Nb-16Ti displayed superior properties, possessing the lowest corrosion current density and widest passivation region, attributed to the addition of Ti. The blood compatibility test illustrated that the Zr-16Nb-xTi materials were nonhemolytic, and the platelets maintained a spherical shape, with no aggregation or activation on Zr-16Nb-xTi. Overall, Ti addition has obvious effects on the developed Zr-16Nb-xTi alloys, and Zr-16Nb-4Ti exhibited low magnetic susceptibility, low modulus, good biocompatibility and proper corrosion properties, demonstrating the potential of use as implant biomaterials.