Formulation of Metal–Organic Framework Inks for the 3D Printing of Robust Microporous Solids toward High-Pressure Gas Storage and Separation
Jérémy Dhainaut, Mickaële Bonneau, Ryota Ueoka, Kazuyoshi Kanamori, Shuhei Furukawa
Abstract
The shaping of metal–organic frameworks (MOFs) has become increasingly studied over the past few years, because it represents a major bottleneck toward their further applications at a larger scale. MOF-based macroscale solids should present performances similar to those of their powder counterparts, along with adequate mechanical resistance. Three-dimensional printing is a promising technology as it allows the fast prototyping of materials at the macroscale level; however, the large amounts of added binders have a detrimental effect on the porous properties of the solids. Herein, a 3D printer was modified to prepare a variety of MOF-based solids with controlled morphologies from shear-thinning inks containing 2-hydroxyethyl cellulose. Four benchmark MOFs were tested for this purpose: HKUST-1, CPL-1, ZIF-8, and UiO-66-NH2. All solids are mechanically stable with up to 0.6 MPa of uniaxial compression and highly porous with BET specific surface areas lowered by 0 to −25%. Furthermore, these solids were applied to high-pressure hydrocarbon sorption (CH4, C2H4, and C2H6), for which they presented a consequent methane gravimetric uptake (UiO-66-NH2, ZIF-8, and HKUST-1) and a highly preferential adsorption of ethylene over ethane (CPL-1).