Effect of SLM Processing Parameters on Microstructures and Mechanical Properties of Al0.5CoCrFeNi High Entropy Alloys
Kun Sun, Weixiang Peng, Longlong Yang, Liang Fang
Abstract
Selective laser melting (SLM) to fabricate Al0.5CoCrFeNi high entropy alloys with pre-mixed powders was studied in this paper. The influences of process parameters including laser power, scanning speed, and hatch spacing on the relative density of high-entropy alloys (HEAs) were investigated. A relative density of 99.92% can be achieved by optimizing the SLM process parameters with laser power 320 W, scanning speed 800 mm/s, and hatch spacing of 60 μm, respectively. Moreover, the microstructure of the HEAs was also studied using scanning electron microscopy (SEM) and x-ray diffraction (XRD). It was found that the microstructure of the HEAs was only composed of face-centered cubic and body-centered cubic phases, without complex intermetallic compounds. The mechanical properties of the HEAs were also characterized. At ambient temperature, the alloys had a high yield strength of about 609 MPa, tensile strength about 878 MPa, and hardness about 270 HV. Through a comparison with the corresponding alloys fabricated by vacuum induction melting, it can be concluded that the high entropy alloys fabricated by SLM had fine microstructures and improved mechanical properties.