Low-temperature solvent-based 3D printing of PLGA: a parametric printability study
Emad Naseri, Haley Butler, Wyatt MacNevin, Marya Ahmed, Ali Ahmadi
Abstract
In this paper, a novel low-temperature 3 D printing technique is introduced and characterized through a parametric printability study to fabricate poly-lactic-co-glycolic acid (PLGA) constructs using methyl ethyl ketone (MEK) as a solvent. The effects of varying concentrations of PLGA in MEK solvent, lactic to glycolic ratio of PLGA, the molecular weight of PLGA, and the scaling of PLGA constructs on the printability are investigated. PLGA concentrations of higher than 80% w/v, lactic to glycolic ratio more than 75%, molecular weight more than 100 kDa, and printing through nozzles smaller than 0.96 mm internal diameter are recommended for 3 D printing of PLGA constructs with high shape fidelity. Ultimately, a vacuum drying solvent removal process is implemented, and Proton Nuclear Magnetic Resonance (1H-NMR) spectroscopy is used to confirm complete removal of the solvent from PLGA constructs. The results of this study can be used for the development of drug-eluting implants.