Protective and Flame-Retardant Bifunctional Epoxy-Based Nanocomposite Coating by Intercomponent Synergy between Modified CaAl-LDH and rGO
Hassan Murtaza, Jingmao Zhao, Mohammad Tabish, Jingbao Wang, Muhammad Mubeen, Jingfan Zhang, Sheng Zhang, Baomin Fan
Abstract
Extensive utilization in various settings poses extra requirements of coatings beyond just anticorrosion properties. Herein, 8-hydroxyquinoline (8-HQ) intercalated CaAl-based layered double hydroxide (CaAl-8HQ-LDH) was loaded on reduced GO (rGO) through a one-pot hydrothermal reaction, which was employed as the nanofiller endowing the epoxy (EP/CaAl-8HQ LDH@rGO) with excellent flame-retardancy while ensuring efficient protection for mild steel. Results of electrochemical impedance spectroscopy (EIS) demonstrated the durability of the EP/CaAl-8HQ LDH@rGO-coated specimen, with the impedance at the lowest frequency (| Z | 0.01Hz ) maintained as 1.84 × 10 10 Ω cm 2 after 120 days of immersion in a 3.5 wt % NaCl solution. Even for the scratched EP/CaAl-8HQ LDH@rGO system, only a slight decline in | Z | 0.01Hz was observed during 180 h of exposure to the NaCl solution, indicating a self-healing feature supported by salt spray tests. UL-94 burning tests revealed the V-0 rating for EP/CaAl-8HQ LDH@rGO with improved thermostability. Strong physical barrier from two-dimensional rGO and the release of 8-HQ from LDH interlayers accounted for the anticorrosive and self-healing properties. However, O 2 -concentration dilution and charring-layer promotion governed the flame-retardant behavior of the nanocomposite coating. The intercomponent synergy of nanofillers achieved in this work may provide a useful reference for designing multifunctional coatings.