Structural, Electronic, and Optical Properties of CsPb(Br1−xClx)3 Perovskite: First-Principles Study with PBE–GGA and mBJ–GGA Methods
Hamid M. Ghaithan, Z.A. Alahmed, Saif M. H. Qaid, Abdullah S. Aldwayyan
Abstract
The effect of halide composition on the structural, electronic, and optical properties of CsPb(Br1−xClx)3 perovskite was investigated in this study. When the chloride (Cl) content of x was increased, the unit cell volume decreased with a linear function. Theoretical X-ray diffraction analyses showed that the peak (at 2θ = 30.4°) shifts to a larger angle (at 2θ = 31.9°) when the average fraction of the incorporated Cl increased. The energy bandgap (Eg) was observed to increase with the increase in Cl concentration. For x = 0.00, 0.25, 0.33, 0.50, 0.66, 0.75, and 1.00, the Eg values calculated using the Perdew–Burke–Ernzerhof potential were between 1.53 and 1.93 eV, while those calculated using the modified Becke−Johnson generalized gradient approximation (mBJ–GGA) potential were between 2.23 and 2.90 eV. The Eg calculated using the mBJ–GGA method best matched the experimental values reported. The effective masses decreased with a concentration increase of Cl to 0.33 and then increased with a further increase in the concentration of Cl. Calculated photoabsorption coefficients show a blue shift of absorption at higher Cl content. The calculations indicate that CsPb(Br1−xClx)3 perovskite could be used in optical and optoelectronic devices by partly replacing bromide with chloride.