Local stress control to suppress dislocation generation for pseudomorphically grown AlGaN UV-C laser diodes
Maki Kushimoto, Ziyi Zhang, Akira Yoshikawa, Koji Aoto, Yoshio Honda, Chiaki Sasaoka, L. J. Schowalter, Hiroshi Amano
Abstract
Previously reported UV-C laser diode (LD) structures have been subject to design constraints owing to dark line defects at the edge of the mesa stripe after device fabrication. To address this issue, a detailed analysis revealed that the dark line defects were dislocations generated by local residual shear stresses associated with mesa formation on highly strained epitaxial layers. A technique for controlling the local concentration of shear stress using a sloped mesa geometry was proposed based on insight gained by modeling the stress distribution at the edge of the mesa stripe. Experimental results showed that this technique succeeded in completely suppressing the emergence of dark-line defects. This technique will be useful in improving the performance of pseudomorphic AlGaN/AlN-based optoelectronic devices, including UV-C LDs.