Optimization of several surface treatment processes for alleviating fretting damage of a locking pin
Jifan He, Zhenbing Cai, Yan‐Ping Ren, Jinfang Peng, Jianhua Liu, Minhao Zhu
Abstract
Abstract The operational safety and reliability of a variable gauge train are affected by the anti-fretting wear performance of the locking mechanism. The main purpose of this study is to optimize the surface treatment process for a locking pin material under actual service conditions to alleviate fretting damage. Based on the two basic principles of surface strengthening and friction reduction, a substrate (AISI 4135 steel) surface was treated by laser quenching (LQ), plasma nitriding (PN), and bonded MoS 2 coating. Systematic fretting wear tests were conducted, and the wear behavior and damage mechanism of various treated surfaces were comprehensively investigated. The results indicate that the wear resistances of the LQ- and PN-treated surfaces were significantly improved, and their main wear mechanisms were abrasive wear, delamination, and oxidation wear. The MoS 2 coating exhibits the lowest friction coefficient and energy dissipation due to its self-lubricating property, but it incurs the highest wear rate and failure in the form of plastic deformation. Furthermore, the rough compound layer with a high hardness on the PN-treated surface is conducive to the formation and maintenance of the third-body contact at the fretting interface, consequently resulting in a significant reduction in wear. An optimal surface treatment process for alleviating fretting damage of the locking pin is recommended via comprehensive evaluation, which provides a reference for the anti-fretting protection of related mechanical components.