Microstructure and Properties of Laser Surface Remelting AlCoCrFeNi2.1 High-Entropy Alloy
Jingrun Chen, Jing Zhang, Ke Li, Dong-Dong Zhuang, Qianhao Zang, Hongmei Chen, Yandi Lu, Bo Xu, Yan Zhang
Abstract
In this study, laser surface remelting of an AlCoCrFeNi2.1 high-entropy alloy was performed using a Yb:YAG laser. The effects of laser surface remelting on the phase structure, microstructure, Vickers hardness, frictional wear properties, and corrosion resistance of the high-entropy alloy were investigated. The remelted layer of the AlCoCrFeNi2.1 high-entropy alloy was produced by remelting at 750 W laser power and formed a good metallurgical bond with the substrate. The X-ray diffraction results showed that the 750 W remelted layer consisted of face-centered cubic and body-centered cubic phases, which were consistent with the phases of the as-cast AlCoCrFeNi2.1 high-entropy alloy, and a new phase was not generated within the remelted layer. Laser surface remelting is very effective in refining the lamellar structure, and the 750 W remelted layer shows a finer lamellar structure compared to the matrix. The surface hardness and wear resistance of the AlCoCrFeNi2.1 high-entropy alloy were substantially improved after laser surface remelting. In a 3.5 wt.% NaCl solution, the laser-remelted surface had a larger self-corrosion potential and smaller self-corrosion current density, and the corrosion resistance was better than that of the as-cast high-entropy alloy.