Stability and performance of in-situ formed phosphosilicate nanoparticles in phosphoric acid-doped polybenzimidazole composite membrane fuel cells at elevated temperatures
Zehua Wang, Jin Zhang, Shanfu Lu, Yan Xiang, Zongping Shao, San Ping Jiang
Abstract
One of the effective strategies to pursue the highly durable high-temperature polymer electrolyte membrane fuel cells (HT-PEMFCs) is to introduce inorganic fillers to the phosphoric acid-doped polybenzimidazole (PA/PBI) membranes. Among the inorganic fillers, phosphates such as phosphosilicate are effective in mitigating acid loss at elevated temperatures (200–300 °C). In this paper, the effect of in situ formed phosphosilicate on the performance and stability of SiO2/PA/PBI composite membranes is studied in detail. The mechanical properties and electrochemical performances of the in situ formed SiO2/PA/PBI membranes depend strongly on the content of in situ formed Si5P6O25 fillers and its distribution and microstructure in the membrane. Such in situ formed SiO2/PA/PBI composite membranes show a high conductivity of 53.5 mS cm−1 at 220 °C. The assembled single cell shows a maximum peak power density (PPD) of 530.6 mW cm−2 and excellent stability at elevated temperature of 220 °C for over 130 h. The exceptional stability at 220 °C is most likely due to the existence of predominant amorphous phosphosilicate phases in the in situ formed SiO2/PA/PBI composite membranes, which inhibits the evaporation and leaching of PA at elevated temperatures. The results indicate the practical application of in situ formed SiO2/PA/PBI composite membranes for HT-PEMFCs.