Influence of cathodic polarization on stress corrosion cracking susceptibility of 35CrMo steel for high strength bolt in simulated deep-sea environment
Rongrong Zhao, Likun Xu, Yonglei Xin, Junji Xuan, Shuangfeng Bai, Lili Xue, Li Li, Yizheng Teng, Mingshuai Guo, Jian Hou, Weimin Guo, Bingzhi Li
Topics & Concepts
Hydrogen embrittlementCathodic protectionStress corrosion crackingMaterials scienceCorrosionMetallurgySeawaterCorrosion fatigueArtificial seawaterPolarization (electrochemistry)CrackingFatigue limitHydrogenComposite materialElectrochemistryChemistryGeologyOceanographyElectrodeOrganic chemistryPhysical chemistryHydrogen embrittlement and corrosion behaviors in metalsCorrosion Behavior and InhibitionWelding Techniques and Residual Stresses