Properties and Durability Performance of Lightweight Fly Ash Based Geopolymer Composites Incorporating Expanded Polystyrene and Expanded Perlite
Dimitrios Kioupis, Aggeliki Skaropoulou, S. Tsivilis, Glikeria Kakali
Abstract
In this study, the use of expanded polystyrene and expanded perlite as lightweight aggregates for the preparation of lightweight geopolymers is tested. The geopolymers’ performance was evaluated through physical, mechanical and thermal testing. Polypropylene fibers were used as reinforcement agents, while the long-term durability was assessed though repeated wet–dry and freeze–thaw cycles and sorptivity tests. The results showed that the introduction of lightweight aggregates in the geopolymer mixes decreased the compressive and flexural strength of the specimens by 77% and 35%, respectively. However, the density and thermal conductivity were substantially improved because of the addition of low-density aggregates. The fiber reinforcement of lightweight samples led to a drastic increase in flexural strength by 65%, leaving unaffected the compressive strength and density of the specimens. The freeze–thaw and sorptivity tests were also improved after the introduction of both aggregates and fibers. Lightweight geopolymer composites exhibiting density in the range of 1.0–1.6 g/cm3, compressive strength of 10–33 MPa, flexural strength of 1.8–6.3 MPa, thermal conductivity of 0.29–0.42 W/mK, and sorptivity of 0.031–0.056 mm/min0.5 were prepared.